Although 8021 aluminum foil as battery collector has many advantages, there are still a series of problems to be solved in the process of application. Firstly, the rigidity of 802 aluminum foil leads to the limitation of its contact area with cathode materials, which affects the internal resistance of cathode wafers; secondly, the bonding strength of 802 aluminum foil is limited with binder and active substance, and the change of electrode volume in cyclic charging and discharging leads to the loosening of particle bonding and easy to fall off, which accelerates the rapid decline of the battery capacity and cycling life; lastly, the oxidized decomposition products of the electrolyte trigger the electrochemical reaction on the surface of aluminum foil, which leads to the corrosion of the aluminum foil. Finally, the oxidized decomposition products of electrolyte cause electric reaction on the surface of aluminum foil, which leads to corrosion of aluminum foil. In order to overcome these problems, aluminum foil must be modified.
Mekanik Properti dari Aluminium Foil Paduan 8021
| Tarik kekuatan% 09% 09% 09 σb (MPa) |
Perpanjangan δ10 (%) |
Bekam tes nilai (mm) | Nota |
| 90-110 | 13-18 | 6.2-7.3 | Erichsen Tes |
Teknis Parameter dari Aluminium Foil Paduan 8021
| Paduan Tidak. | Si | Fe | Cu | Mn | Mg | Zn | Lain | Al |
| 8021 | Kurang dari atau sama ke 0.15 | 1,2 Kurang dari atau sama ke | Kurang dari atau sama dengan % 7b{0}}.05 | Kurang dari atau sama dengan % 7b{0}}.05 | Kurang dari atau sama dengan % 7b{0}}.05 | Kurang dari atau sama dengan % 7b{0}}.05 | Kurang dari atau sama dengan % 7b{0}}.05 | TINGGAL |
| Kurang dari atau sama ke 1,7 | ||||||||
| 8021 aluminium foil | ||||||||
| Produk | Jenis | Marah | Ketebalan (mm) | Lebar(mm) | ||||
| 8021 Baterai Film Foil | O /H*2 /H*4 | 0.035-0.055 | 100-1600 | Menyesuaikan | ||||
| 8021 Farmasi Foil | H14 /H18 | 0.018-0.2 | 100-1600 | |||||
| 8021 Kemasan Foil | O /H22 /H24 | 0.018-0.2 | 100-1600 | Menyesuaikan | ||||
Arang permukaan lapisan adalah the utama modifikasi metode% 2c yang bisa secara signifikan meningkatkan internal resistensi dari aluminium foil.802 The utama modifikasi metode untuk aluminium foil termasuk permukaan perawatan (misalnya% 2c kimia etsa% 2c elektrokimia etsa% 2c DC anodisasi% 2c corona perawatan), konduktif pelapis pelapis (misalnya, berlapis karbon, graphene-dilapisi, karbon nanotube-dilapisi, komposit pelapis), 3D berpori struktur (mis. , busa, pita nano, nano-kerucut, serat kepang), dan komposit modifikasi. dan komposit modifikasi. Ini metode permainan a kunci peran dalam peningkatan kinerja dari aluminium foil dan meningkatkan konektivitas dari elektroda bahan.